Fracture-Toughness Analysis in Transition-Temperature Region of Three American Petroleum Institute X70 and X80 Pipeline Steels

摘要

The fracture toughness in the transition-temperature region of three American Petroleum Institute (API) X70 and X80 pipeline steels was analyzed in accordance with the American Society for Testing and Materials (ASTM) E1921-05 standard test method. The elastic-plastic cleavage fracture toughness (K_(Jc)) was determined by three-point bend tests, using precracked Charpy V-notch (PCVN) specimens; the measured K_(Jc) values were then interpreted by the three-parameter Weibull distribution. The fracture-toughness test results indicated that the master curve and the 98 pct confidence curves explained the variation in the measured fracture toughness well. The reference temperatures obtained from the fracture-toughness test and index temperatures obtained from the Charpy impact test were lowest in the X70 steel rolled in the two-phase region, because this steel had smaller effective grains and the lowest volume fraction of hard phases. In this steel, few hard phases led to a higher resistance to cleavage crack initiation, and the smaller effective grain size led to a higher possibility of crack arrest, thereby resulting in the best overall fracture properties. Measured reference temperatures were then comparatively analyzed with the index temperatures obtained from the Charpy impact test, and the effects of microstructures on these temperatures were discussed.