Measurement of Gibbs energy of formation of LaGaO_3 using a composition-graded solid electrolyte

摘要

A composition-graded solid electrolyte (LaF_3)_y centre dot (CaF_2_(1-y) was used for the measurement of the standard Gibbs energy of formation of LaGaO_3 from its component oxides. An equimolar mixture of CaO and CaF_2 was employed as the reference electrode. The composition of the working electrode depended on temperature. A three-phase mixture of LaGaO_3 + Ga_2O_3 + LaF_3 was used in the temperature range from 910 to 1010 K, while a mixture of LaGaO_3 + Ga_2O_3 + LaO_(1-x)F_(1+2x) was employed from 1010 to 1170 K. Both the reference and working electrodes were placed under pure oxygen gas. Because of the high activity of LaF_3 at the working electrode, there was significant diffusion of LaF_3 into CaF_2. The composition-graded electrolyte was designed to minimize the electrode-electrolyte interaction. The concentration of LaF_3 varied across the solid electrolyte; from y = 0 near the reference electrode to a maximum value y = 0.32 at the working electrode. For the correct interpretation of the electromotive force at T> 1010 K, it was necessary to use thermodynamic properties of the lanthanum oxyfluoride solid solution. The standard Gibbs energy of formation of LaGaO3 from its component oxides according to the reaction, 1/2La_2O_3 (A-rare earth) + 1/2Ga_2O_3 (#beta#) -> LaGaO_3 (rhombohedral) can be represented by the equation: #DELTA#G_(f,(ox))~o/j mol~(-1) = -46 230+7.75 T/K (+-1500).