Dry sliding wear behaviour of hypereutectic Al–Si piston alloys containing iron-rich intermetallics

摘要

The effect of iron-rich intermetallics on the wear behaviour of Al–Si hypereutectic alloys has been studied. Dry sliding wear tests have been conducted using a pin-on-disk machine under different normal loads of 18, 51, 74 and 100 N and at a constant sliding speed of 0.3 m/s. The addition of 1.2 wt.% Fe to the LM28 alloy increased the wear rate due to the formation of needle beta intermetallics. Introducing 0.6 wt.% Mn to the iron-rich alloy changed the beta intermetallics into the modified alpha phases, and therefore reduced the detrimental effect of iron. TIG welding method as a surface melting process was applied on the iron and manganese containing alloy and led to a fine microstructure and increased the wear resistance.