Susceptibility of highly alloyed austenitic stainless steels to caustic stress corrosion cracking

摘要

Slow Strain Rate tests (5 × 10{sup}6 to 4× 10{sup}(-6) s{sup}(-1)) in 300 g/L sodium hydroxide at 200 ℃ were conducted on highly alloyed austenitic stainless steels with various nickel and chromium concentrations: N08904 (2OCr-25Ni-4Mo), N8825 (22.5Cr-4ONi-3Mo), N08028 (27Cr-3ONi-3.5Mo), R20033 (32.5Cr-31Ni-1.5Mo). Stress Corrosion Cracking (SCC) resistance of studied alloys increases in the following order: N08904→N8825→N08028→R20033 in accordance with increasing chromium content. The SCC susceptihility indexes decrease gradually with decreasing of strain rate. In materials exhibiting higher SCC resistance, tests shouldbeconducted at very low strain rates (ε{top}(·) <2 × 10{sup}(-7) s{sup}(-1)) to observe indications of SCC. When silphide ions are added the R20033 steel exhibiting an excellent corrosion behaviour in pure caustic solution, becomes highly susceptible to SCC, even at ε{top}(·) = 5 × 10{sup}(-6) s{sup}(-1).