Life prediction method of copper thin film repaired by laser irradiation based on healing variable

摘要

The cyclic stress-strain constitutive relationships for copper film smooth specimens with different damage degrees before and after laser irradiation treatment were investigated. Compared with the changes of the constitutive relationships under different damage degrees, a healing variable for the repaired copper film by laser irradiation was defined. Based on the analysis of the healing variable, a fatigue life prediction method was proposed. The experimental lives of the damaged notched specimens after laser irradiation treatment were used to verify the proposed life prediction method. The results showed that the predicted lives are in good agreement with the experimental results.