The Effect of Prolonged Thermo-oxidative Ageing on the Mechanical Properties of Dynamically Vulcanized Poly(Vinyl Chloridel/Nitrile Butadiene Rubber Thermoplastic Elastomers

摘要

Plasticized poly(vinyl chloride)itrite butadiene rubber(PVC/NBR)thermoplastic elastomers(TPEs)were dynamically vulcanized in the melt stage with the incorporation of a semi-efficient vulcanizing system using a Brabender Plasticor-der at 1SOdeg C and 50 rpm rotor speed.Curative concentration was progressively increased from 0 to 1 part per hundred(phr)NBR in order to study the effect of dynamic curing on the plasticized blend.The mechanical properties investigated include tensile strength,elongation at break(%EB),modulus at 100% elongation(M100),tear strength,and hardness.The effect of thermo-oxidative ageing(TOA)on the mechanical properties was investigated by exposing the PVC/NBR TPEs in an air oven at 100deg C for 3,7,14,and 21 days.It was found that tensile and tear strength passed through a maximum value,whereas,hardness and M100 increased steadily with the sulfur content and ageing time.On the contrary,the elongation at break reduced gradually with ageing time until it reaches a minimum value.The increase in crosslink density as well as the steady reduction in swelling index with increasing concentration of curatives provided an excellent evidence for the significant increase in crosslink density with ageing time.The changes in physical and mechanical properties of the TPEs is believed to be closely related to some microstructural changes taking place as a result of the formation of new crosslinks due to prolonged thermo-oxidative environment.