Experimental study of the impact damage on an Al2O3-coated glass under stress

摘要

The impact damage of an Al2O3-coated soda-lime glass under tensile and compressive stress conditions was investigated by an impact test using a steel ball (2min dia.). The size of the glass specimens was 40x40x5(mm). In order to change the porosity percent of each specimen, the target distance was set at 120mm and 70mm. Also, the effect of the thickness of the coating layer was shown by two amounts (100 mu m and 50 mu m). The velocity of the steel balls was set between 30 and 60m/s. After the impact test, the crack patterns and lengths were measured using a stereo-microscope. The tensile and compressive specimens were prepared by inflation and deflation of air pressure within a pressure vessel. It was confirmed that the crack length of the glass under tensile stress was longer than that of glass under compressive stress. Also, the optimum conditions were a target distance of 70mm and 100 mu m of a coating thickness, thus resulting in a minimization of porosity percent and area.