Highly efficient and stable transparent electromagnetic interference shielding films based on silver nanowires

摘要

Transparent electromagnetic interference (EMI) shielding materials with high optical transmittance and outstanding shielding effectiveness (SE) for optoelectronic devices in visual windows are urgently needed. Herein, we demonstrate the preparation of a transparent EMI shielding film based on silver nanowires (Ag NWs)viaa facile Mayer-rod coating method. The electrical conductivity and transmittance of Ag NW-based films can be greatly improved through treatment with NaBH(4)and the lamination of poly(diallyldimethyl-ammonium chloride). The coverage of the polymer decreases the surface roughness, with no damage on the uniform mesh of the Ag NWs. The Ag NW/PDDA composite films present a sheet resistance of 22 omega sq(-1)at a transmittance of 95.5%, better than that of commercial indium tin oxide (ITO). The excellent optoelectrical performance of the Ag NW/PDDA composite film is further ascertained by fitting the transmittance with the resistance, with a figure of merit of 443. The Ag NW/PDDA composite films in this study exhibit greatly improved stability during 25 degrees C/65% RH aging for 35 days with the assistance of the coverage layer. Moreover, the EMI SE of the Ag NW/PDDA composite films is 28 dB on average at a transmittance of 91.3%, and continuously increases to 31.3 dB while the optical transmittance is still maintained at 86.8%, which is superior to those of most reported transparent EMI shielding materials. Taken together, the excellent optical transmittance and EMI shielding performance of the Ag NW/PDDA composite film make it an outstanding transparent EMI shielding material in optoelectronic devices, such as aerospace equipment, medical devices, communication facilities, and electronic displays.