Biocompatibility, induction of mineralization and antimicrobial activity of experimental intracanal pastes based on glass and glass-ceramic materials

摘要

Aim To evaluate the biocompatibility, induction of mineralization and antimicrobial activity of experimental intracanal pastes based on two glass and glass-ceramic materials. Calcium hydroxide (Ca(OH)(2)) paste was used as the positive control. Methodology The glass-ceramic powder [two-phased Biosilicate (BS-2P)] and F18 bioactive glass were mixed with distilled water (ratio 2 : 1), inserted in polyethylene tubes and implanted in the subcutaneous tissues of 16 rats. Empty tubes were used as negative control. After 7 and 30 days (n = 8), the rats were euthanized for haematoxylin-eosin, von Kossa, polarized light and osteopontin (OPN) immunolabeling analysis. Direct contact tests using a suspension of each paste were performed withEnterococcus faecalisplanktonic cells to evaluate antimicrobial activity (24 h of contact), in a pilot study. The number of CFU mL(-1)was calculated for each group. The antimicrobial analysis data were submitted to one-wayanovaand Tukey tests, whilst biocompatibility and immunohistochemical data were submitted to the Kruskal-Wallis and Dunn tests (P 0.05). At 30 days, most specimens of control, F18 and BS-2P groups had mild inflammation, whilst Ca(OH)(2)had mild to moderate inflammation; however, no differences were determined amongst the groups (P > 0.05). The fibrous capsule was thick at 7 days, becoming thin at 30 days. All pastes induced von Kossa-positive structures and were birefringent to polarized light. At seven days, the BS-2P group had significantly more OPN immunolabeling compared to the control and Ca(OH)(2)groups (P < 0.05). At 30 days, the F18 group had significantly more OPN immunolabeling compared to the control and Ca(OH)(2)groups (P < 0.05). All pastes reduced the total number ofE. faecalis; however, the reduction was only significant when comparing BS-2P and Ca(OH)(2)groups to the control (P < 0.05). Only calcium hydroxide eliminatedE. faecalis. Conclusions Experimental BS-2P and F18 pastes were biocompatible, stimulated biomineralization and induced significant OPN immunolabeling compared to Ca(OH)(2). Only the BS-2P paste demonstrated antimicrobial activity comparable to Ca(OH)(2).