Porous alumina ceramics with enhanced mechanical and thermal insulation properties based on sol-treated rice husk

摘要

To improve the properties of porous alumina ceramics, which were typically prepared by adding pore-forming agents, rice husk (RH) as pore-forming agent was pretreated with zirconia sol. The effects of sol-treatment on the thermal conductivity and compressive strength of the resultant ceramics were characterized. Furthermore, the pore size distribution, pore shape, microstructure, and phase evolution also were studied. The results showed that the RH pretreatment optimizes the microstructure of the ceramic pores. Moreover, complete morph-genetic RH is clearly observed in the pores, which is established as a key factor in improving the properties of the resultant ceramic. The thermal insulation properties are determined to significantly improve, although the thermal conductivity increases slightly with the increment of zirconia sol concentration from 5 to 10 wt%. Meanwhile, after sintering at 1550 degrees C, the compressive strength is significantly greater for the specimen prepared with 10 wt% zirconia sol-treated RH (65.56 MPa) than that with untreated RH (43.37 MPa). Hence, it was demonstrated that the use of zirconia sol-pretreated RH as a pore-forming agent could enhance the mechanical and thermal insulation properties of porous alumina ceramics.