Development of spinel opaque glazes for ceramic tiles

摘要

The feasibility of developing fast-firing opaque wall tile glazes obtained from zircon-free frits was studied. The structural and morphological characteristics of the glazes were determined by differential scanning calorimetry, an optical dilatometer, X-ray diffraction and scanning electron microscopy. The studied glaze was characterized by a high whiteness value L* greater than 94, very low values of a* and b* which is about -0.65 and 0.01, respectively, and a high gloss value above 98%. The opaque effect is due to the presence of spine! crystals with a size range of 0.2-1.0 mu m, which is formed by devitrification during fast-firing. The Vickers micro-hardness of the studied glaze is higher than the one of the commercial zircon based glass-ceramic glazes. This type of frit can be an alternative one for fabricating opaque ceramic glazes.