Sintering kinetics of disperse ultrafine equiaxed alpha-Al2O3 nanoparticles

摘要

The sintering kinetics of ceramic nanoparticles is essential for preparing dense nanocrystalline ceramics with fine grains, but the sintering kinetics of disperse ultrafine alpha-Al2O3 nanoparticles has not been systematically explored so far. In this paper, the sintering kinetics of disperse ultrafine equiaxed alpha-Al2O3 nanoparticles with a mean particle size of 4.5 nm and a narrow size distribution of 2-8 nm without any agglomeration was studied systematically. Finally, alpha-Al2O3 nanocrystalline ceramic with a mean grain size of 36 nm and a relative density of 99.7% was sintered in air by two-step sintering (heated to 1100 C without hold and then cooled down to 950 degrees C with a 40 h hold). The sintering temperature is the lowest for pressureless sintering of alpha-Al2O3 and almost fully dense alpha-Al2O3 nanocrystalline ceramic obtained also has the finest grain so far. (C) 2017 Elsevier Ltd. All rights reserved.