Effect of Lead-Bismuth Eutectic Oxygen Concentration on the Onset of Dissolution Corrosion in 316?L Austenitic Stainless Steel at 450?°C

摘要

This work focuses on the effect of dissolved oxygen concentration in liquid lead-bismuth eutectic (LBE) on the onset of dissolution corrosion in a solution-annealed 316?L austenitic stainless steel. Specimens made of the same 316?L stainless steel heat were exposed for 1000?h at 450?°C to static liquid LBE with controlled concentrations of dissolved oxygen, i.e., 10 ~( ?5 ) , 10 ~( ?6 ) , and 10 ~( ?7 ) mass%. The corroded 316?L steel specimens were analyzed by scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). A complete absence of dissolution corrosion was observed in the steel specimens exposed to liquid LBE with 10 ~( ?5 ) and 10 ~( ?6 ) mass% oxygen. In the same specimens, isolated “islands” of FeCr-containing oxides were also detected, indicating the localized onset of oxidation corrosion under these exposure conditions. On the other hand, dissolution corrosion with a maximum depth of 59? μ m was detected in the steel specimen exposed to liquid LBE with 10 ~( ?7 ) mass% oxygen. This suggests that the threshold oxygen concentration associated with the onset of dissolution corrosion in this 316?L steel heat lies between 10 ~( ?6 ) and 10 ~( ?7 ) mass% oxygen for the specific exposure conditions (i.e., 1000?h, 450?°C, static liquid LBE).