Multiple Melting Behavior of High-Speed Melt Spun Polylactide Fibers

摘要

High-speed melt spinning of polylactide (PLA) was conducted and the structure and multiple melting behavior of the as-spun fibers were investigated. In the analysis of temperature modulated differential scanning calorimetry (TMDSC) thermograms for the as-spun PLA fibers taken-up at 1 and 6 km/min, the peaks around the melting temperature region in the reversing heat flow (RHF) and nonreversing heat flow (NRHF) curves were mainly separated into (1) a pair of an endothermic peak (Peak L) in RHF and an exothermic peak (Peak R) in NRHF in a low temperature region, (2) an endothermic peak (Peak M) both in RHF and NRHF (only in RHF for PLA fiber spun at the low-speed) in an intermediate temperature region, and (3) an endothermic peak (Peak H) both in RHF and NRHF in a higher temperature region. Wide-angle X-ray diffraction (WAXD) measurements were conducted during the heating process of the as-spun fibers cut into powders. In the case of fibers obtained at 1 km/min, disordered crystals, i.e. -form crystals, were formed through cold crystallization followed by a disorder-to-order phase transition, i.e. to crystalline modification, with partial melting of the crystals around 148.5 degrees C in the temperature range of Peaks R and L. Finally, the form crystals melted above 169.4 degrees C, in the temperature range of Peak H. On the other hand, the PLA crystals generated by the orientation-induced crystallization during the spinning process at a spinning velocity of 6 km/min did not show a WAXD profile of perfect form crystals but showed an intermediate structure having lattice spacings between the and forms. Such intermediate crystals did not transformed into form crystals during the heating process.