Comparison of effect of shot-peening with HFMI treatment or use of LTT consumables on fatigue strength of 1300 MPa yield strength steel weldments

摘要

In this paper, T-joint samples in a 1300 MPa yield strength steel were produced using conventional or low transformation temperature (LTT) type consumables. The welded samples were either subjected to high-frequency mechanical impact (HFMI) treatment or to shot-peening. Fatigue testing was performed under fully reversed, constant amplitude bending load. Shot-peening gave a significant increase in fatigue strength for more than around 50,000 cycles. Shot-peened LTT welds had the highest fatigue strength, with conventional welds being shot-peened having slightly lower fatigue strength. HFMI treatment of conventional and LTT welds improved the fatigue strength also, but to a lesser extent, keeping the slope in the SN diagram close to three, while shot-peened samples had a slope of 5-7. Significant differences in compressive residual stress were seen between the different welds, with the most compressive stress found in the shot-peened samples. This was probably one of the main reasons for the improved fatigue life of shot-peened samples.