Optical Properties of Silver Halide Photochromic Glasses Doped with Cobalt Oxide

摘要

Photochromic glasses having composition (SiO2)(45)(B2O3)(35)(Al2O3)(7.5)(Na2O)(12.5)(AgBr), (Cu2O) doped with (CoO)(x) , in which, x = 0, 0.006, 0.02 and 0.07 g were prepared using the conventional melt technique. The amorphous nature of these glass samples was confirmed using X-ray diffraction analysis at room temperature. The absorption measurements in the infrared region of the spectrum were recorded in the wave number range (4000-400) cm(-1). Spectral reflectance and transmittance at normal incidence of the prepared glass samples were recorded with a spectrophotometer in the spectral range 200-2500 nm. Experimental and theoretical densities of the prepared glass samples were measured, calculated and compared. Analytical expressions were used to calculate the real and imaginary parts of the refractive indices. Dispersion parameters such as: single oscillator energy, dispersion energy, average oscillator wavelength, and Abbe's number were deduced and compared. Absorption dispersion parameters such as: optical energy gap for direct and indirect transitions, Urbach energy and steepness parameter were calculated. Effects of doping with cobalt oxide CoO as a transition metal on linear and predicted nonlinear optical parameters were investigated and interpreted. Experimental results indicate that there is an optimum concentration of cobalt doping around 0.006 g. The optical band gap decreases with increasing doping and causes an increase in nonlinear optical parameters. Doping with cobalt oxide improves the linear and nonlinear optical properties of the prepared glasses.