In-situ Formation and Densification of MgAl2O4-Y3Al5O12 and MgAl2O4-MgNb2O6 Ceramics via a Single-stage SRS Process

摘要

MgAl2O4 (MA)-Y3Al5O12 (YAG) and MA-MgNb2O6 (MN) ceramics with high density were successfully fabricated via a single-stage solid-state reaction sintering (SRS) process at 1580 degrees C for 4 h. The effect of Y2O3 or Nb2O5 additions from 2.5 wt% to 7.5 wt% on the phase compositions, microstructures, shrinkage ratio, apparent porosity, bulk density and cold compressive strength of MA-YAG and MA-MN ceramics has been investigated. It was found that MgO and Y2O3 reacted with Al2O3 to form MA and YAG during sintering while Nb2O5 reacted with MgO to form MN.