Preparation of carbon quantum dots based high photostability luminescent membranes

摘要

Urethane acrylate (UA) was used to prepare carbon quantum dots (C-dots) luminescent membranes and the resultants were examined with FT-IR, mechanical strength, scanning electron microscope (SEM) and quantum yields (QYs). FT-IR results showed the polyurethane acrylate (PUA) prepolymer -C=C-vibration at 1101cm(-1) disappeared but there was strong vibration at1687cm(-1)which was contributed from the-C=O groups in cross-linking PUA. Mechanical strength results showed that the different quantity of C-dots loadings and UV-curing time affect the strength. SEM observations on the cross-sections of the membranes are uniform and have no structural defects, which prove that the C-dots are compatible with the water-soluble PUA resin. The C-dot loading was increased from 0 to 1g, the maximum tensile stress was nearly 2.67MPa, but the tensile strain was decreased from 23.4% to 15.1% and 7.2% respectively. QYs results showed that the C-dots in the membrane were stable after 120h continuous irradiation. Therefore, the C-dots photoluminescent film is the promising material for the flexible devices in the future applications.