Influence of two different cement space settings and three different cement types on the fit of polymer-infiltrated ceramic network material crowns manufactured using a complete digital workflow

摘要

Objectives The study evaluates the influence of two spacer settings and three resin luting materials on the marginal and internal fit of polymer-infiltrated ceramic network (PICN) material crowns manufactured using a complete digital workflow. Methods Optical impressions of fifty identical dies were performed using the 3M scanner (software version 5.0.2). Twenty crowns were designed using Ceramill Mind (version 3.4.10.1163), from which ten with spacer setting of 50 mu m (G1) and ten with 80 mu m (G2). Thirty crowns (spacer setting of 50 mu m) were divided into three groups corresponding to the resin materials used as follows: RelyX Unicem (RX), Variolink Esthetic (VLE), and Nexus 3 (NX3). All crowns were milled from Vita Enamic blocks. After micro-CT scanning, absolute marginal discrepancy (AMD), internal gap (IG), total cement space volume (TCV), and marginal porosities (VP) were measured. Results Significant difference was detected on the VP between the RX and NX3 group (p = 0.033). The mean values of all parameters were the following: AMD (mu m): G1 182.6, G2 253.7, RX 210.8, VLE 195.5, NX3 186.6; IG (mu m): G1 215.6, G2 173.1, RX 171.1, VLE 198.6, NX3 203; TCV (mm(3)): G1 22.9, G2 20.49, RX 17.57, VLE 17.49, NX3 20.59; VP (mm(3)): G1 0.26, G2 0.34, RX 0.32, VLE 0.46, NX3 0.54. Conclusions Fit of PICN material crowns was not significantly influenced by increasing the spacer settings and cementation with different resin materials. Additionally, RelyX Unicem showed significantly less porosities as compared with Nexus3.