Comparison of thermoset soy protein resin toughening by natural rubber and epoxidized natural rubber

摘要

Fully bio-based soy protein isolate (SPI) resins were toughened using natural rubber (NR) and epoxidized natural rubber (ENR). Resin compositions containing up to 30 wt % NR or ENR were prepared and characterized for their physical, chemical and mechanical properties. Crosslinking between SPI and ENR was confirmed using H-1-NMR and ATR-FTIR. All SPI/NR resins exhibited two distinctive drops in their modulus at glass transition temperature (T-g) and degradation temperature (T-d) at around -50 and 215 degrees C, corresponding to major segmental motions of NR and SPI, respectively. SPI/ENR resins showed similar T-g and T-d transitions at slightly higher temperatures. For SPI/ENR specimens the increase in ENR content from 0 to 30 wt % showed major increase in T-g from -23 to 13 degrees C as a result of crosslinking between SPI and ENR. The increase in ENR content from 0 to 30 wt % increased the fracture toughness from 0.13 to 1.02 MPa with minimum loss of tensile properties. The results indicated that ENR was not only more effective in toughening SPI than NR but the tensile properties of SPI/ENR were also significantly higher than the corresponding compositions of SPI/NR. SPI/ENR green resin with higher toughness could be used as fully biodegradable thermoset resin in many applications including green composites. (C) 2016 Wiley Periodicals, Inc.