Morphology evolution of a thermotropic liquid-crystalline polymer in a polyamide 6,6 matrix regulated by graphene

摘要

A two-step process, thermotropic liquid-crystalline polymer (TLCP) premixing with reduced graphene oxide (RGO) followed by blending with polyamide 6,6 (PA66), was used to prepare ternary TLCP/RGO/PA66 blends. The rheological behaviors, morphology, and mechanical properties of the blends were investigated. The results show that RGO migrated from the TLCP phase to the interface between the TLCP and PA66 phase during melt blending; this was due to a similar affinity of the RGO nanosheets to both component polymers. The dimensions of the dispersive TLCP domains were markedly reduced with the mounting RGO content; this revealed a good compatibilization effect of RGO on the immiscible polymers. The hierarchical structures of the TLCP fibrils were found in both the unfilled TLCP/PA66 blends and TLCP/RGO/PA66 blends. This supposedly resulted from the extensional and torsional action of unstable capillary flow. With the addition of RGO, the viscosities of the blends decreased further, and the fibrillation of TLCP and the mechanical performance of TLCP composites were both enhanced. (C) 2016 Wiley Periodicals, Inc.