Fabrication of three-dimensional nanostructured titania materials by prism holographic lithography and the sol-gel reaction

摘要

We present a simple, easy method for fabricating high-quality titania inverted replicas of 3D holographically featured structures. A combination of single-prism holographic lithography and sol-gel chemistry was used to prepare 3D titania inverse structures with flat and completely open surfaces without the use of additional postprocessing steps, such as reactive ion etching, ion-beam milling, and/or polishing steps. A hydrophobic, stable liquid titania precursor facilitated the complete infiltration of the precursor into the hydrophobic 3D SU-8 polymer template, which produced very uniform high-quality titania inverse structures. Although the degree of film shrinkage during the calcination process was large (～34%), the optical strength of the 3D titania inverse photonic crystals doubled because of the high-refractive-index contrast. Compared to titania inverse opal structures, the filling fraction (～27%) of titania materials has been doubled. This is the first work to fabricate titania inverse photonic crystals with a high filling fraction by utilizing prism holographic lithography and the sol-gel chemistry reaction of a stable titania precursor. The X-ray diffraction patterns indicated the presence of a crystalline anatase or rutile phase depending on the calcination temperature.