Occurrence of intercalation of PCE superplasticizers in calcium aluminate cement under actual application conditions, as evidenced by SAXS analysis

摘要

Intercalation of polycarboxylate (PCE) superplasticizers in calcium aluminate cement (CAC) during early hydra-tion under both idealized and actual application conditions was confirmed by small-angle X-ray scattering (SAXS) analysis. The CaAl-PCE-LDHs were characterized by XRD, TEM, SEM and elemental analysis, and exhibited interlayer distances (d-values) ranging from 5 to 24 nm, owed to the polydispersity of the PCE samples! Intercalating ability of the PCEs was dependent on their grafting density and anionicity, but was independent of their molecular weights. When highly anionic PCEs were utilized, significant amounts of nanocrystalline, colloidal intercalates were recovered, while few intercalates were detected when less anionic PCEs possessing high graft density were employed. Thus, contrary to OPC, less anionic PCEs disperse CAC better as little amount is wasted via intercalation, whereas higher dosages are required for more anionic PCEs, owed to abundant formation of organo-mineral phases. Finally, recommendations for reliable analysis of PCE intercalates in cement are given.