Study on grain growth of fine grained WC-Co hardmetal by numerical calculation

摘要

This paper reviews our simulation study by numerical calculation based on two-, three and multi-grain-size models on WC grain growth in fine grained WC-Co hardmetal doped with VC. The study aimed to presume or predict the following: (1) the cause and conditions for the abnormal grain growth which occurs in some cases in the fine gralned hardmetal prepared from fine WC powders with mean grain size below about 0.2 μm, and (2) how the mean grain size of the hardmetal varies with decreasing mean grain size of the WC starting powder to 0.1μm or nano-meter size. The calculation results by these three kinds of models suggested the following, respectively: (1) the occurrence of the abnormal grain growth is generally substantial for WC starting powder with bimodal size-distribution and mean grain size below 0.1～0.2 μm, and not due to the non-uniform distribution of the grain growth inhibitor, (2) the introduction of middle grains caused the disappearance of small (fine) grains during sintering, leading to abruptly increase of the mean grain size of alloy, and (3) the mean grain size of alloy becomes so large as about 0.3～0.4μm, even when the WC starting powders with nano- size as well as 0.1 μm are used.