Plasma spraying of functionally graded yttria stabilized zirconia/NiCoCrAlY coating system using composite powders

摘要

Pre-alloyed and plasma spheroidized composite powders were used as the feedstock in the plasma spraying of functionally graded yttria stabilized zirconia (YSZ)/NiCoCrAlY coatings. The ball milling parameters of the composite powders and the plasma spraying parameters for preparing functionally graded materials (FMGs) coatings were optimized to obtain the best performance for the thermal barrier coatings (TBCs). Microstructure, physical, mechanical, and thermal properties of YSZ/NiCoCrAlY FGMs coatings were investigated and compared with those of traditional duplex coatings. Results showed that the advantages of using pre-alloyed composite powders in plasma spraying were to ensure chemical homogeneity and promote uniform density along the graded layers. Microstructure observation showed the gradient distribution of YSZ and NiCoCrAlY phases in the coating, and no clear interface was found between two adjacent different layers. Oxidation occurred during plasma spray and the resultant aluminum oxide combines with YSZ in a wide range of proportions. The bond strength of functionally graded coatings was about twice as high as that of the duplex coatings because of the significant reduction of the residual stresses in the coatings. The thermal cycling resistance of functionally graded coating was much better than that of duplex coating.