High-pressure spark plasma sintering (SPS) of transparent polycrystalline magnesium aluminate spinel (PMAS)

摘要

A high pressure SPS (spark plasma sintering) process was applied for consolidation of un-doped polycrystalline magnesium aluminate spinel. This approach allows fabricating a fully dense transparent ceramic with submicron grain size and high hardness values at a relatively low temperature (1200 °C). The light transmittance of the specimens increases with increasing applied pressure, while the hardness gradually decreases. The optimal combination of properties was achieved after sintering at 1200 °C at a heating rate of 5°/min, a holding time of 15 min and an applied pressure of 350-400 MPa. The specimens display the level of transmittance in the visible wavelengths and hardness values comparable with the best results reported in the literature for the two-stage fabrication process (pressureless sintering and hot isostatic pressing).