Gelcasting and pressureless sintering of silicon carbide ceramics using Al_2O_3-Y_2O_3 as the sintering additives

摘要

In this paper, silicon carbide ceramics were prepared by aqueous gelcasting and pressureless sintering using Al_2O_3 and Y_2O_3 as the sintering additives. In order to develop well dispersed SiC slurries in the presence of sintering additives, the AI2O3 and Y_2O_3 powder was treated in the cilric acid solution in advance. Zeta potential measurement showed that the isoelectric point (IEP) of AI2O3 and Y2O3 powder moved toward low. pH region after treatment. Rheological measurement confirmed that the addition of as-treated powder showed very limited influence on the slurry properties as compared to that of untreated powder. SiC slurries with solid content of 54 vol% and enough fluidity can be developed. After gelcasting and pressureless sintering, SiC ceramics with nearly full density, fine grained and homogeneous microstructurc can be obtained. Results showed that the surface treatment of Al_2O_3 and Y_2O_3 with citric acid is effective for the gelcasting process of SiC.