Preparation and Pore Structure Stability at High Temperature of Porous Fe-Al Intermetallics

摘要

Porous Fe-Al intermetallics with different nominal compositions (from Fe-8 wt.% Al to Fe-50 wt.% Al) were fabricated by Fe and Al elemental powders through reaction synthesis. The effects of the Al content on the pore structure properties, and the comparison of pore structure stabilities at high-temperatures among the porous Fe-Al intermetallics and porous Ti, Ni, 316L stainless steel samples, were systematically studied. Results showed that the open porosity, maximum pore size, and permeability vary with the Al content. Porous Fe-(25-30 wt.%) Al intermetallics show good shape controllability and excellent pore structure stability at 1073 K in air, which suggests that these porous Fe-Al intermetallics could be used for filtration at high temperatures.