A lanthanide-doping route to aspect-ratio-controlled KSc2F7 nanocrystals for upconversion, downconversion and magnetism

摘要

A novel route was developed by doping rare-earth ions (RE~(3+)) with large ionic radii (such as La~(3+), Ce~(3+), Sm~(3+), Eu~(3+), Tb~(3+), Dy~(3+), Yb~(3+) and Lu~(3+) for aspect ratio modification of KSc2F7 nanocrystals (NCs). The results revealed that the shape of the nanocrystals could be readily tuned from one-dimensional long nanorods to zero-dimensional ultrasmall nanospheres. The aspect ratio of the NCs could be adjusted over a broad range from 45 to 1 by changing the dopant or doping concentration. Interestingly it was found that doping of a lanthanide with a larger ionic radius was equivalent to increasing the amount of the dopant on the aspect ratio evolution. The NCs doped with different RE~(3+) also exhibited multifunctionality, including upconversion (UC) and downconversion (DC) emissions as well as paramagnetic properties.