It is well known that a - B -+ a phase transformation in titanium proceeds with a definite orientation relationship between parent and product phases, i.e. the Burgers' relationship [1], namely, {110} || (0 001)n, and (111) || (1120)ff. Because of the crystal symmetry, starting with a single component of texture in a phase, a total of 72 reorientations are possible with equal probability after the double 展开▼