Stress and failure analyses of scarf repaired CFRP laminates using a cohesive damage model

摘要

This study describes stress and failure analyses of tensile loaded repaired Carbon Fibre Reinforced Composite(CFRP)laminates,using scarf configuration.A numerical model including interface finite elements was used to obtain peel and shear-stress distributions in the directions tangent and normal to the scarf.These stresses were evaluated at several locations in the repair,namely in the middle of the adhesive,at interfaces between adhesive and patch,and between adhesive and parent material.Several scarf angle values were considered in the analysis.A cohesive mixed-mode damage model was also used to carry out the failure analysis,in order to assess the efficiency of the repairs,for different stacking sequences.A study was performed to evaluate the influence of the mechanical properties of the adhesive and parent laminate/adhesive and adhesive/patch interfaces on the strength and failure modes of the joint.It was concluded that the strengths of the adhesive and interfaces are more important than the fracture properties in the failure process of the repair.It was also verified that the strength of the repair increased exponentially with the scarf angle reduction.