Rheological Effects of the Incorporation of Chlorinated Polyethylene Compatibilizers in a HDPE/PVC Blend

摘要

Small-amplitude oscillatory measurements, creep and recoil experiments, capillary extrusion flow and shrinkage measurements have been performed to elucidate the effect of block and random chlorinated polyethylene (CPE) on the rheological properties of a ternary high density polyethylene (HDPE)/poly(vinyl chloride) (PVC)/CPE system.It is observed that the storage modulus, the complex viscosity and the steady state viscosity at low shear rates decrease when a small amount of CPE is incorporated to 50/50 (wt.) HDPE/PVC binary blend. However, at high shear rates, in experiments performed in extrusion flow, the trend is reversed, and the incorporation of CPE to the binary blend increases viscosity. The high melt elasticity of HDPE is severely reduced when this polymer is mixed with PVC, but when CPE is included as a third component, elastic recovery is considerably increased. All these rheological results, which are independent of type (block or random) of CPE used, are explained considering the morphological changes produced by CPE and during extrustion flow.