Covulcanisation of natural rubber and chlorobutyl rubber - effect of curative diffusion between phases and ZnCl{sub}2 addition

摘要

Natural rubber (NR) and chlorobutyl rubber (CuR) were compounded with various formulations containing tetramethyithiuram disulphide (TMTD), sulphur, and ZnO, and masterbatches of these compounds were blended in a 70 : 30 NR/CIIR ratio and vulcanized in a press at 150 ℃. Crosslink densities of vulcanisates were determined by swelling and tensile properties measured. In formulations in which the concentration gradient permitted the diffusion of TMTD and sulphur to a CuR phase containing ZnO, tensile strengths were slightly better than 70% of the values of NR compounds of similar crosslink densities. In formulations in which TMTD and sulphur diffused to the faster curing NR phase, blend properties were also better than 70% of those of NR compounds, but at higher crosslink densities, tensile strengths and elongation at break decreased in parallel. This was attributed to failure in a layer of more highly crosslinked material formed within the NR phase close to the interface. Although ZnCI2 can crosslink CuR to NR, thus ensuring good interfacial bonding, the addition of ZnCl2 to the CuR masterbatch led to attack on the TMTD accelerator and a significant reduction in crosslink density and tensile properties of blends.