Impact of a Structure on Durability of Modified Nickel-Base Superalloys in Creep Conditions/ Wp?yw Struktury Na Trwa?o?? W Warunkach Pe?zania Modyfikowanych Nadstopów Na Bazie Niklu

摘要

The study assesses the impact of surface and bulk modification and filtration during pouring on a durability under accelerated creep conditions of casts made of IN-713C and MAR-247 nickel superalloys scrap used for manufacturing of aircraft engine parts. The impact of solutionizing (1185°C/2 h) with subsequent ageing (870°C/20 h) on the creep resistance of a casting made from MAR-247 coarse-grained superalloy was also examined. Morphological structure parameters were determined with the use of Met-Ilo software. Macrostructure analysis of casts showed very significant impact of surface modification treatment. Creep test results clearly showed that coarse grained samples of IN-713C and MAR-247 superalloys have higher creep resistance. Moreover alloy MAR-247 had higher creep durability after heat treatment compared to as-cast state.