STRUCTURAL MODIFICATION OF PA 6 AND PA 6 FIBRES

摘要

The contribution deals with synthesis and properties of copolyamides from e-caprolactam and two nylon salts: one from adipic acid + diethylenetriamine (ADETA) and the other from adipic acid + 1-(2-aminoethyl) piperazine (AN2) and utilisation of these copolyamides as additives for fibre-forming PA 6. Apparent viscosity of blend melts PA 6/copolyamide was measured and PA 6 fibres modified with each of prepared copolyamide were prepared. Mechanical properties - tensile strength, elongation and Young modulus of non modified and modified PA 6 fibres were evaluated and compared.%Príspevok sa zaoberá syntézou a vlastnosťami kopolyamidov z ε-kaprolaktámu a dvoch nylonových solí: nylonovej soli kyseliny adipovej a dietyléntriamínu (ADETA) a nylonovej soli kyseliny adipovej a 1-(2-aminoethyl) piperazine /AN2) a ich využitím ako aditív pre vláknotvorný PA 6.rnBola stanovená zdanlivá viskozita zmesných tavenín PA 6/kopolyamid a boli pripravené PA 6 vlákna modifikované 10 a 30% hm. každého kopolyamidu. Mechanické vlastnosti - pevnost', ťažnosť a Youngov modul nemodifikovaných a modifikovaných PA 6 vlákien boli porovnané. Získané výsledky dovol'ujú konstatovat', že:rn1. Kopolyamidy sú semikryštalinické a ich molová hmotnost' je ovplyvnená najmä obsahom minoritných komonomérov ADETA a AN2. Čím vyšší je celkový obsah komonomérov tým nižšia je molová hmotnost' kopolyamidu. Nylonová sol' ADETA má nepriaznivý vplyv na molovu hmotnost'.rn2. Termické charakteristiky - teplota tavenia, entalpia tavenia, teplota a entalpia kryštalizácie odrážajú vyššiu neusporiadanosť makromolekúl kopolyamidu a sú nižšie.rn3. Zdanlivé viskozity zmesných tavenín sú nižšie ako zdanlivá viskozita taveniny PA 6.rn4. Pri dížiacom pomere λ=3 je pevnost' PA 6 vláken modifikovaných 10% hm. kopolyamidov s vyššou molovou hmotnosťou najmenej na úrovni nemodifikovaných PA 6 vlákien.