Polymer Material Based on Shale Phenols

摘要

A polymer material with cohesion and adhesion strengths of 4.15 and 4.90 MPa, respectively, was prepared based on a composition of shale phenols. The specific elongation was 170%. Product lifetimes from 7 to 13 years were determined for filled and unfilled polymers, respectively, using accelerated thermal ageing. The polymer can be used as a repair and lining material.