Below Grade Coated Direct Imbedded Steel Pole Corrosion Failures With Solutions

William A. Byrd

首页> 外文期刊>Power and Energy Technology Systems Journal, IEEE >Below Grade Coated Direct Imbedded Steel Pole Corrosion Failures With Solutions

【24h】

Below Grade Coated Direct Imbedded Steel Pole Corrosion Failures With Solutions

机译：低于等级涂层的直接埋入式钢管腐蚀故障及其解决方案

获取原文

获取原文并翻译 | 示例

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

页面导航

摘要
著录项
相似文献
相关主题

摘要

A history and descriptions of below grade coated direct imbedded steel pole corrosion failures is presented. Examples of actual coated steel pole corrosion failures are shown. The methods of the corrosion attacks are disclosed. A cost effective cathodic protection scheme for mitigating the below grade steel pole corrosion is presented.

机译：介绍了低级涂层直接埋入式钢杆腐蚀失败的历史和描述。显示了实际的涂层钢杆腐蚀失败的示例。公开了腐蚀侵蚀的方法。提出了一种经济有效的阴极保护方案，用于减轻以下级别的钢杆腐蚀。

著录项

来源
《Power and Energy Technology Systems Journal, IEEE》 |2019年第1期|41-46|共6页
作者
William A. Byrd;
展开▼
作者单位

Columbia Corrosion Control Co. Columbia SC USA;

展开▼
收录信息
原文格式 PDF
正文语种 eng
中图分类
关键词
Steel; Corrosion; Coatings; Anodes; Copper; Poles and towers; Zinc;

机译：钢;腐蚀;涂料;阳极;铜;杆和塔;锌锌;
入库时间 2022-08-18 04:32:16

相似文献

外文文献
中文文献
专利

1. Influence of Fe3+?Diffusion on the Rate of Corrosion of Carbon Steel Imbedded in Porous Media in Acidic Solutions [J] . F.A.Albatati, Y.O.Fouad, M.H.Abdel-Aziz, International Journal of Electrochemical Science . 2020,第11期

机译：Fe3 +的影响 - 酸性溶液多孔介质中掺入碳钢腐蚀速率的影响
2. An electrochemical impedance spectroscopy study of the corrosion behaviour of PVD coated steels in 0.5 N NaCl aqueous solution: Part Ⅱ. EIS interpretation of corrosion behaviour [J] . C. Liu, Q. Bi, A. Leyland, Corrosion science . 2003,第6期

机译：电化学阻抗谱研究PVD涂层钢在0.5 N NaCl水溶液中的腐蚀行为：第二部分。 EIS腐蚀行为的解释
3. Corrosion and stress corrosion cracking initiation of grade 304 and 316 stainless steels in activated Methyl Diethanol Amine (aMDEA) solution [J] . Panahi H., Eslami A., Golozar M. A. Journal of natural gas science and engineering . 2018,第期

机译：活化甲基二乙醇胺（AmdeA）溶液中304和316级不锈钢的腐蚀和应力腐蚀裂解起始
4. Quantifying Corrosion at the Interface of Coated Steel and Identifying the Significant Properties from Polymer Coatings that Mitigate the Corrosion Process in the Presence of a Defect during Immersion in Saline Solution [C] . Christopher J. Scanlon, James W. Rawlins Annual international waterborne, high-solids, and powder coatings symposium . 2020

机译：量化涂层钢界面处的腐蚀，并鉴定来自聚合物涂层的显着性质，在盐水溶液中存在缺陷时减轻腐蚀过程的腐蚀过程
5. Study of corrosion-induced failure mechanisms of epoxy-coated reinforcing steel [D] . Lee, Seungkyoung 1994

机译：环氧涂层钢筋腐蚀引起的破坏机理研究
6. NN′-DialkylcystineGemini and Monomeric N-Alkyl Cysteine Surfactantsas Corrosion Inhibitors on Mild Steel Corrosion in 1 M HCl Solution:A Comparative Study [O] . Ruby Aslam, Mohammad Mobin, *, 2017

机译：NN-二烷基胱氨酸双子座和单体N-烷基半胱氨酸表面活性剂作为在1 M HCl溶液中对低碳钢腐蚀的缓蚀剂：比较研究
7. Influence of Fe3+ Diffusion on the Rate of Corrosion of Carbon Steel Imbedded in Porous Media in Acidic Solutions [O] . F A. Albatati 2020

机译：Fe3 +扩散对酸性溶液多孔介质掺入纤维型碳钢速率的影响
8. Corrosion Behavior of A216 Grade WCA Mild Steel and Ti Grade 12 Alloy in Hydrothermal Brines: Salt Repository Project: Annual Report, FY 1986. [R] . Westerman, R. E., Haberman, J. H., Pitman, S. G., 1988

机译：a216级WCa低碳钢和Ti 12级合金在热液盐水中的腐蚀行为：盐库项目：年度报告，1986年。

Below Grade Coated Direct Imbedded Steel Pole Corrosion Failures With Solutions

摘要

著录项

相似文献

相关主题

期刊订阅