Poly(divinylbenzene) Microencapsulated Octadecane for Use as a Heat Storage Material: Influences of Microcapsule Size and Monomer/Octadecane Ratio

摘要

Poly(divinylbenzene) (PDVB) microencapsulated octadecane (OD) (PDVB/OD) used as heat storage material were prepared by suspension polymerization at 70°C using benzoyl peroxide and polyvinyl alcohol as initiator and stabilizer, respectively. The influence of microcapsule size and divinylbenzene (DVB)/OD weight ratio on the microcapsule shape and thermal properties of encapsulated OD were considered. Thermal properties and thermal stability of PDVB/OD microcapsules were determined using differential scanning calorimeter (DSC) and thermogravimetric analyzer. The optical micrographs and scanning electron micrographs showed that the microcapsules have spherical shape only in the case of 50/50 (%w/w) of DVB/OD whereas they were nonspherical with the decreasing of DVB content. However, the core materials were still well encapsulated even increasing the OD content to 70%wt. From DSC analysis, in all cases, the melting temperature of encapsulated OD (28°C) was almost the same as that of bulk OD (30°C), yet it was quite different in the case of crystallization temperature (≤ 19°C and 25°C for encapsulated and bulk OD, respectively). The latent heats of melting and crystallization of encapsulated OD, in all conditions, were reduced from those of bulk OD (242 and 247 J/g, respectively).View full textDownload full textKeywordsHeat storage material, Microencapsulation, Poly(divinylbenzene), Radical polymerization, Thermal propertiesRelated var addthis_config = { ui_cobrand: "Taylor & Francis Online", services_compact: "citeulike,netvibes,twitter,technorati,delicious,linkedin,facebook,stumbleupon,digg,google,more", pubid: "ra-4dff56cd6bb1830b" }; Add to shortlist Link Permalink http://dx.doi.org/10.1080/03602559.2012.694949