Effects of hypochlorite treatment on the surface morphology and mechanical properties of polyethersulfone ultrafiltration membranes

摘要

Polyethersulfone membranes are widely used for ultraflltration and microfiltration especially in the dairy industry, but they are believed to degrade when exposed to the sodium hypochlorite solution that is used to sanitize the processing equipment. Such membranes were exposed to sodium hypochlorite for up to 25,000 ppm-day at 55℃, and pH 9 and 12. Mechanical properties as measured by dynamic mechanical analysis and tensile strength did not change greatly, but surface properties measured by FTIR-ATR, field emission scanning electron microscopy and associated energy dispersive X-ray spectroscopy detected significant changes in the surface. Surface pitting was observed and was found to be most severe at pH 9. It was thought that pitting was the likely cause of degradation in performance of the membranes and that pits could act as stress raisers leading to cracking.