Synthesis And Uv Absorption Properties Of 2,3-dihydroxynaphthalene-6-sulfonate Anion-intercalated Zn-al Layered Double Hydroxides

摘要

State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology, P.O. Box 98, Bei San Huan Dong Lu 15, Chao Yang District, Beijing 100029, ChinarnAn organic UV absorbent has been intercalated into a layered double hydroxide (LDH) host by ion exchange of a Zn-Al-LDH-nitrate precursor with a solution of 2,3-dihydroxynaphthalene-6-sulfonic acid (DNSA) sodium salt in water. After intercalation of the UV absorbent, the powder X-ray diffraction (XRD) pattern shows that the interlayer distance in the LDHs increases from 0.90 to 1.59 nm. The possible structure is that the interlayer DNSA anions arrange in a monolayer and in a perpendicular orientation toward the hydroxide layers. Infrared spectra and TG-DTA curves reveal the presence of a complex system of supramolecular host-guest interactions between layers. The thermal stability of the intercalated UV absorbent was investigated by TG-DTA and it was found that this material is more stable than the original organic UV absorbent at high temperature, showing that the thermostability is markedly enhanced after intercalation into the LDH host. The UV absorbent-intercalated LDHs exhibit excellent UV photostability in polypropylene composites.