A Eutectoid Reaction for the Decomposition of Austenite into Pearlitic Lamellae of Ferrite and M₂₃C₆ Carbide in a Mn-Al Steel

摘要

We discovered a eutectoid reaction in an Fe-13.4Mn-3.0Al-0.63C (wt pct) steel after solution heat treatment at 1373 K (1100 °C) and holding at temperatures below 923 K (650 °C). The steel is single austenite at temperatures from 1373 K to 923 K (1100 °C to 650 °C). A eutectoid reaction involves the replacement of the metastable austenite by a more stable mixture of ferrite and M₂₃C₆ phases at temperatures below 923 K (650 °C). The mixture of ferrite and M₂₃C₆ is in the form of pearlitic lamellae. The morphology of the lamellae of the product phases is similar to that of pearlite in steels. Thus, we found a new pearlite from the eutectoid reaction of the Mn-Al steel featuring γ → α + M₂₃C₆. A Kurdjumov–Sachs (K-S) orientation relationship exists between the pearlitic ferrite (α) and M₂₃C₆ (C6) grains, i.e., (110)_α // (111)_C6 and [[`1] overline{1} 11]<sub>α</sub> // [0[`1] overline{1} 1]_C6. The upper temperature limit for the eutectoid reaction is between 923 K and 898 K (650 °C and 625 °C).