机译:熔覆合金AA3003 / AA6xxx薄板弯曲弯曲失效分析
Department of Mechanical Engineering, McMaster University, 1280 Main Street West, Hamilton, Ontario, Canada L8S 4L7;
Novelis Global Technology Center, P.O. Box 8400, Kingston, Ontario, Canada K7L 5L9,CanmetMATERIALS, Natural Resources Canada, 183 Long-wood Road South, Hamilton, Ontario. Canada L8P 0A5;
Department of Mechanical Engineering, McMaster University, 1280 Main Street West, Hamilton, Ontario, Canada L8S 4L7;
Aluminum Materials Consultants, 106 Nicholsons Point Road, Bath, Ontario, Canada K0H 1G0;
Department of Mechanical Engineering, McMaster University, 1280 Main Street West, Hamilton, Ontario, Canada L8S 4L7;
Aluminum; Bendability; Modeling; Crack; Finite element method;
机译:人工老化后具有不同覆层厚度的Fusion AA3003 / AA6xxx板材的弯曲性改善
机译:AA6xxx铝合金板弯曲性能的晶粒度建模
机译:通过表面形貌的数值分析表征AA6xxx合金薄板上的绳索
机译:通过表面形貌的数值分析表征AA6xxx合金薄板上的绳索
机译:空隙损伤和剪切带发展对AA6111汽车铝合金板弯曲性的影响。
机译:最终轧制温度对等通道角轧制和连续弯曲制备的AZ31合金板微结构和力学性能的影响
机译:双轴拉伸下AA3003铝合金板材的织构