Microstructure and magnetism in barium strontium titanate (BSTO)-barium hexaferrite (BaM) multilayers

摘要

High quality multilayers of barium ferrite (BaM) and barium strontium titanate (BSTO) were grown in optimized conditions on thermally oxidized Si(100) and Al_2O_3 substrates using magnetron sputtering. As-grown films were amorphous and different annealing procedures were explored to stabilize crystalline phases. BSTO and BaM phases were identified using X-ray diffraction and cross-sectional scanning electron micrographs showed sharp interfaces between BSTO and BaM layers. Magnetic hysteresis loops obtained at various temperatures and field orientations showed a large coercivity (～2500 Oe) consistent with the hard magnetic hexaferrite component. Hysteresis loops also revealed the distinct influence of magnetocrystalline and shape anisotropies at different temperature ranges.