Ti-based amorphous alloys with a wide supercooled liquid region

摘要

Ti-Cu-Ni-Co quaternary amorphous alloys produce by melt spinning were found to have a wide supercooled liquid region before crystallization, though no glass transition was observed in Ti-Cu binary amorphous alloys. The largest temperature interval of the supercooled liquid region (ΔT_x) is as large as 90 K for Ti_(50)Cu_(25)Ni_(20)Co_5. There is a tendency for ΔT_x to increase with an increase in storage modulus and with a decrease in loss modulus. It is therefore presumed that the increase in ΔT_x for the multicomponent amorphous alloy is due to the suppression of crystallization for the supercooled liquid resulting from the increase in viscosity.