Effect of stress distribution on the tool joint failure of internal and external upset drill pipes

摘要

Detailed investigation was carried out on the tool joint failure of the internal & external upset (IEU) GSS105 drill pipes. Stresses were analyzed using 2D finite element method (FEM) for the threaded tool joint of the drill pipe under the combined loading conditions containing preload, tensile and bending loads. The stress concentration factors in the pin and box were calculated. Results showed that the maximum stress concentration occurred at the roots of the first tooth from the pin tool joint shoulder of the drill pipe. Fractographic observation revealed that the tool joint failure of the drill pipe was caused by fatigue crack nucleated at the tooth root and propagated through the wall of the tool joint. The deterioration of the fatigue resistance of the tool joint is related to dogleg region where severe cyclic bending load exists due to the local deviation of the drill pipe from the vertical line.