Determination of thermal parameters of glasses from the system Bi_x(As₂S₃)_100−x based on DSC curves

摘要

Thermal properties of glasses from the system Bi _x (As₂S₃)_100−x were studied by differential scanning calorimetry of a representative series of samples with x = 0.5, 2, 4, 6, 8, and 10 at.% Bi by determining the characteristic temperatures (T _g, T _onset, T _c, T _m) and enthalpies (H _c, H _m) of the processes taking place in the samples during their thermal treatment. Analysis of DSC recordings for the samples at the same heating rate allowed characterization of the phase transition temperature T _g as a function of the content of doping atoms in accordance with the criteria of chemical bonds formation in amorphous materials. Samples with 4 and 6 at.% Bi were thermally treated at different heating rates with the aim of determining, among the others, the parameters of their thermal stability. The assessment was done based on three different criteria. A higher tendency toward crystallization was observed with the glasses having a higher Bi content. Also, a trend of T _g shifting toward higher values, observed with increase in the heating rate, is in concordance with the Lasocka equation.