Preparation of highly stable TiO₂ sols and nanocrystalline TiO₂ films via a low temperature sol–gel route

摘要

Highly stable TiO₂ sols were prepared by adjusting the water-to-titanium molar ratio to ~4 in the process of hydrolysis and condensation of titanium isopropoxide in ethanol with HNO₃. Particularly, long-term stable TiO₂ sols were prepared without adding any chemical additives. Anatase TiO₂ nanocrystallites with sizes of 3–5 nm in diameter were uniformly dispersed in the stable sol. Crystallized TiO₂ films were successfully deposited on Si (100) using the stable sol via a dip-coating process with low temperature curing at as low as 100 °C. The synthesized TiO₂ sols and films are promising for use in flexible or dye-sensitized solar cells.