Restoration of solid oxide fuel cell stacks after failure of partial cells

摘要

We investigated a solid oxide fuel cell stack that employs anode-supported planar cells in which two intermediate plates are installed every 10 cells to determine the influence of the separation and recon-nection of the intermediate plates after high temperature operation. We showed that this separation and reconnection caused no significant degradation in stack performance. A 30-cell stack, which was constructed by removing two 10-cell sub-stacks from a 50-cell stack that had operated stably 1200 h, functioned well. The difference between the average voltages of the cells in the 50- and 30-cell stacks was less than 3% when the current density, fuel utilization, and oxygen utilization were 0.30 A cm~(-2),60%, and 15%, respectively. The 30-cell stack operated stably for about 1200 h with almost no degradation. These findings indicate that our stack can be restored after cells in the stack have broken down simply by removing the 10-cell sub-stacks that contain the broken cells and replacing them with undamaged 10-cell sub-stacks.