Ion-beam synthesis of epitaxial Au nanocrystals in MgO

摘要

The formation of Au nanoclusters in MgO using ion implantation and subsequent annealing was investigated. Approximately 1200 and 1400 Au~(2+) ionsm~2 were implanted in MgO(100) substrates at 300 and 975 K, respectively. Subsequent annealing in air for 10 h at 1275 K promoted the formation of Au nanostructures in MgO. The sample implanted at 300 K showed severe radiation damage. In addition, two-dimensional plateletlike structures with possible composition of Au and MgO were formed during implantation in the sample that was implanted at 300 K. In contrast, Au implantation at 975 K promoted the nucleation of Au nanostructures during implantation. Subsequent annealing of both samples show three-dimensional clusters in MgO. However, the 975 K implanted sample shows clean, high-quality, single-crystal Au clusters that have an epitaxial relationship to MgO(100).