Effect of Mn addition on microstructure and mechanical properties of cast Al-2Li-2Cu-0.8Mg-0.4Zn-0.2Zr alloy

摘要

The effect of 0.5 wt% Mn addition on the microstructure and mechanical properties of cast Al-2Li-2Cu-0.8Mg-0.4Zn-0.2Zr (wt%) alloy was investigated. Results showed that the grain size of Mn-containing alloy was smaller than that of Mn-free alloy in both the as-cast and solution treated state. Al_(20)Mn_3Cu_2 dispersoids were formed during solution treatment in the Mn-containing alloy. After aging at 175 ℃ for 32 h, a large volume fraction of coherent Al_3Li/Al_3(Li, Zr) particles were precipitated in both Mn-free and Mn-containing alloys, while more Guinier-Preston-Bagaratsky zones were observed in the Mn-free alloy. Mn addition improved the elongation significantly, which was 1.7% for Mn-free alloy and 3.3% for the alloy with 0.5 wt% Mn addition.